White Micro Fine Powder Paste PVC Resin (Emulsion Grade)

White Micro Fine Power PVC Paste Resin (Emulsion Grade) 1.LG 1302/1202,P440/P450 2.for leather,flooring 3.technic support

 White Micro Fine Power PVC Paste Resin (Emulsion Grade)  

Product : PVC Paste  Resin (Emulsion PVC Resin)

Formula : (C2H3Cl)n  H.S.CODE : 3904101000

CAS No. : 9002-86-2

 

1.Characteristic:

 

Paste PVC resin is a homopolymer of PVC which is made by emulsion polymerization,it can be used for coating cloth, rotary forming, macerating, spraying and foaming after mixed with plasticizer and other addition agent. It is a light white and micro fine powder .

 

2.Specification:

 

Specs		Type Index
		XBRE-1	XBRE-2	XBRE-3	XBRE-4
Viscosity (Ml/G)		160 Min	155-165	155-145	140-150
K Value		78.0 Min	75.0-79.0	75.0-79.0	73.5-76.0
Polymerization Degree		1850 Min	1750-1950	1550-1750	1475-1650
B-type Viscosity 30° C mpa. s		4.0 Max	3.0-5.0	5.0-7.0	4.0-7.0
Volatile % ≤		0.4	0.4	0.4	0.4
Bulk density, g/cm 3		0.3-0.45
Remain % mg/kg	0.25mm Sieve ≤	0.01	0.01	0.01	0.01
	0.063mm Sieve ≤	0.1	0.1	0.1	0.1
DOP: resin (portion)		60: 100	100: 100	60: 100	100: 100
Apparent		White micro powder

 

3. Application:

XBRE-1: non foaming artificial leather bottom,surface of artificial leather and floor leather,canvas,maceration forming(gloves,boots),rotary forming(toy),hollow forming and rubber, bottle caps.XBRE-2: artificial leather foaming layer,bottle cap(pad),steel plate coating,eraser,formulation with high plasticizer content,maceration forming.XBRE-3:

Mainly used for non-foaming or micro-foaming artificial leather, also be used in coating, glass fiber, macerating, textile printing and general products

XBRE 4: canvas, soft pipe, fabric tablecloth, artificial leather foaming layer 

4.Packing:

 

25kg/bag or as per your requirement.

 

5.Store andtransport:

 

Prevent from rain,snow,humid,sunshine,throwing and other  mechanical damage.

White Micro Fine Powder Paste PVC Resin (Emulsion Grade)